Well-defined N3 C1 -anchored Single-Metal-Sites for Oxygen Reduction Reaction.

N-, C-, O-, S-coordinated single-metal-sites (SMSs) have garnered significant attention due to the potential for significantly enhanced catalytic capabilities resulting from charge redistribution. However, significant challenges persist in the precise design of well-defined such SMSs, and the fundamental comprehension has long been impeded in case-by-case reports using carbon materials as investigation targets. In this work, the well-defined molecular catalysts with N3 C1 -anchored SMSs, i.e., N-confused metalloporphyrins (NCPor-Ms), are calculated for their catalytic oxygen reduction activity. Then, NCPor-Ms with corresponding N4 -anchored SMSs (metalloporphyrins, Por-Ms), are synthesized for catalytic activity evaluation. Among all, NCPor-Co reaches the top in established volcano plots. NCPor-Co also shows the highest half-wave potential of 0.83 V vs. RHE, which is much better than that of Por-Co (0.77 V vs. RHE). Electron-rich, low band gap and regulated d-band center contribute to the high activity of NCPor-Co. This study delves into the examination of well-defined asymmetric SMS molecular catalysts, encompassing both theoretical and experimental facets. It serves as a pioneering step towards enhancing the fundamental comprehension and facilitating the development of high-performance asymmetric SMS catalysts.

Embedding Ru Clusters and Single Atoms into Perovskite Oxide Boosts Nitrogen Fixation and Affords Ultrahigh Ammonia Yield Rate.

Ammonia is a key chemical feedstock worldwide. Compared with the well-known Haber-Bosch method, electrocatalytic nitrogen reduction reaction (ENRR) can eventually consume less energy and have less CO2 emission. In this study, a plasma-enhanced chemical vapor deposition method is used to anchor transition metal element onto 2D conductive material. Among all attempts, Ru single-atom and Ru-cluster-embedded perovskite oxide are discovered with promising electrocatalysis performance for ENRR (NH3 yield rate of up to 137.5 ± 5.8 µg h-1  mgcat -1 and Faradaic efficiency of unexpected 56.9 ± 4.1%), reaching the top record of Ru-based catalysts reported so far. In situ experiments and density functional theory calculations confirm that the existence of Ru clusters can regulate the electronic structure of Ru single atoms and decrease the energy barrier of the first hydrogenation step (*NN to *NNH). Anchoring Ru onto various 2D perovskite oxides (LaMO-Ru, MCr, Mn, Co, or Ni) also show boosted ENRR performance. Not only this study provides an unique strategy toward transition-metal-anchored new 2D conductive materials, but also paves the way for fundamental understanding the correlation between cluster-involved single-atom sites and catalytic performance.

Covalent Triazine Frameworks and Porous Carbons: Perspective from an Azulene-Based Case.

Covalent triazine frameworks (CTFs) are among the most valuable frameworks owing to many fantastic properties. However, molten salt-involved preparation of CTFs at 400-600 °C causes debate on whether CTFs represent organic frameworks or carbon. Herein, new CTFs based on the 1,3-dicyanoazulene monomer (CTF-Azs) are synthesized using molten ZnCl2 at 400-600 °C. Chemical structure analysis reveals that the CTF-Az prepared at low temperature (400 °C) exhibits polymeric features, whereas those prepared at high temperatures (600 °C) exhibit typical carbon features. Even after being treated at even higher temperatures, the CTF-Azs retain their rich porosity, but the polymeric features vanish. Although structural de-conformation is a widely accepted outcome in polymer-to-carbon rearrangement processes, the study evaluates such processes in the context of CTF systems. A proof-of-concept study is performed, observing that the as-synthesized CTF-Azs exhibit promising performance as cathodes for Li- and K-ion batteries. Moreover, the as-prepared NPCs exhibit excellent catalytic oxygen reduction reaction (ORR) performance; hence, they can be used as air cathodes in Zn-air batteries. This study not only provides new building blocks for novel CTFs with controllable polymer/carbon features but also offers insights into the formation and structure transformation history of CTFs during thermal treatment.

Molecular Engineering of CoII Porphyrins with Asymmetric Architecture for Improved Electrochemical CO2 Reduction.

The electrochemical reduction of carbon dioxide (CO2 ) based on molecular catalysts has attracted more attention, owing to their well-defined active sites and rational structural design. Metal porphyrins (PorMs) have the extended π-conjugated backbone with different transition metals, endowing them with unique CO2 reduction properties. However, few works focus on the investigation of symmetric architecture of PorMs as well as their aggregation behavior to CO2 reduction. In this work, a series of CoII porphyrins (PorCos) with symmetric and asymmetric substituents were used as model of molecular catalysts for CO2 reduction. Owing to the electron donating effect of 2,6-dimethylbenzene (DMB), bandgaps of the complexes became narrower with the increasing number of DMB. As electrocatalysts, all PorCos exhibited promising electrocatalytic CO2 reduction performance. Among the three molecules, asymmetric CoII porphyrin (as-PorCo) showed the lowest onset potential of -288 mV and faradaic efficiencies exceeding 93 % at -0.6 V vs. reversible hydrogen electrode, which is highly competitive among the reported state-of-art porphyrin-based electrocatalysts. The CO2 reduction performance depended on π-π stacking between PorCo with carbon nanotubes (CNTs) and adjacent PorCos, which could be readily controlled by atomically positioned DMB in PorCo. Density functional theory calculations also suggested that the charge density between PorCo and CNT was highest due to the weak steric hindrance in as-PorCo, providing the new insight into molecular design of catalysts for efficient electrochemical CO2 reduction.

Boosting the electronic and catalytic properties of 2D semiconductors with supramolecular 2D hydrogen-bonded superlattices.

The electronic properties of two-dimensional semiconductors can be strongly modulated by interfacing them with atomically precise self-assembled molecular lattices, yielding hybrid van der Waals heterostructures (vdWHs). While proof-of-concepts exploited molecular assemblies held together by lateral unspecific van der Waals interactions, the use of 2D supramolecular networks relying on specific non-covalent forces is still unexplored. Herein, prototypical hydrogen-bonded 2D networks of cyanuric acid (CA) and melamine (M) are self-assembled onto MoS2 and WSe2 forming hybrid organic/inorganic vdWHs. The charge carrier density of monolayer MoS2 exhibits an exponential increase with the decreasing area occupied by the CA·M unit cell, in a cooperatively amplified process, reaching 2.7 × 1013 cm-2 and thereby demonstrating strong n-doping. When the 2D CA·M network is used as buffer layer, a stark enhancement in the catalytic activity of monolayer MoS2 for hydrogen evolution reactions is observed, outperforming the platinum (Pt) catalyst via gate modulation.

Quantum Capacitance through Molecular Infiltration of 7,7,8,8-Tetracyanoquinodimethane in Metal-Organic Framework/Covalent Organic Framework Hybrids.

Metal-organic frameworks (MOFs) and covalent organic frameworks (COFs) have been extensively investigated during the last two decades. More recently, a family of hybrid materials (i.e., MOF@COF) has emerged as particularly appealing for gas separation and storage, catalysis, sensing, and drug delivery. MOF@COF hybrids combine the unique characteristics of both MOF and COF components and exhibit peculiar properties including high porosity and large surface area. In this work, we show that the infiltration of redox-active 7,7,8,8-tetracyanoquinodimethane (TCNQ) molecules into the pores of MOF@COF greatly improves the characteristics of the latter, thereby attaining high-performance energy storage devices. Density functional theory (DFT) calculations were employed to guide the design of a MOF@COF-TCNQ hybrid with the TCNQ functional units incorporated in the pores of MOF@COF. To demonstrate potential application of our hybrids, the as-synthesized MOF@COF-TCNQ hybrid has been employed as an active material in supercapacitors. Electrochemical energy storage analysis revealed outstanding supercapacitor performance, as evidenced by a specific areal capacitance of 78.36 mF cm-2 and a high stack volumetric energy density of 4.46 F cm-3, with a capacitance retention of 86.4% after 2000 cycles completed at 0.2 A cm-2. DFT calculation results strongly indicate that the high capacitance of MOF@COF-TCNQ has a quantum capacitance origin. Our liquid-phase infiltration protocol of MOF@COF hybrids with redox-active molecules represents a efficacious approach to design functional porous hybrids.

Topological defect-containing Fe/N co-doped mesoporous carbon nanosheets as novel electrocatalysts for the oxygen reduction reaction and Zn-air batteries.

Developing effective electrocatalysts for the oxygen reduction reaction is of great significance for clean and renewable energy technologies, such as metal-air batteries and fuel cells. Defect engineering is the central focus of this field because the overall catalytic performance crucially depends on highly active defects. For the ORR, topological defects have been proven to have a positive effect. However, because preparation and characterization of such defects are difficult, a basic understanding of the relationship between topological defects and catalytic performance remains elusive. In this study, topological defect-containing Fe/N co-doped mesoporous carbon nanosheets were synthesized using azulene-based sandwich-like polymer nanosheets as the precursor. As electrocatalysts, such porous carbon nanosheets exhibited promising ORR activity, methanol tolerance ability, and stability with a half-wave potential of 841 mV under alkaline conditions, which is superior to those of most of the reported porous carbons. As the air cathode for Zn-air batteries, the catalyst exhibited a peak power density of 153 mW cm-2 and a specific capacity of 628 mA h g-1,which were higher than those of a Pt/C-based Zn-air battery. Density functional theory calculation further proved the positive effect of topological defects on the oxygen reduction activity. These results indicate that bottom-up topological defect engineering could be a new and promising strategy for developing high-performance electrocatalysts.

Catechol-Coordinated Framework Film-based Micro-Supercapacitors with AC Line Filtering Performance.

Coordination polymer frameworks (CPFs) have broad applications due to their excellent features, including stable structure, intrinsic porosity, and others. However, preparation of thin-film CPFs for energy storage and conversion remains a challenge because of poor compatibility between conductive substrates and CPFs and crucial conditions for thin-film preparation. In this work, a CPF film was prepared by the coordination of the anisotropic four-armed ligand and CuII at the liquid-liquid interface. Such film-based micro-supercapacitors (MSCs) are fabricated through high-energy scribing and electrolytes soaking. As-fabricated MSCs displayed high volumetric specific capacitance of 121.45 F cm-3 . Besides, the volumetric energy density of MSCs reached 52.6 mWh cm-3 , which exceeds the electrochemical performance of most reported CPF-based MSCs. Especially, the device exhibited alternating current (AC) line filtering performance (-84.2° at 120 Hz) and a short resistance capacitance (RC) constant of 0.08 ms. This work not only provides a new CPF for MSCs with AC line filtering performance but also paves the way for thin-film CPFs preparation with versatile applications.

B/N-Enriched Semi-Conductive Polymer Film for Micro-Supercapacitors with AC Line-Filtering Performance.

Microsupercapacitors (MSCs) have drawn great attention for use as miniaturized electrochemical energy storage devices in portable, wearable, as well as implantable electronics. Many materials have been developed as electrodes for MSCs. However, the thin-film fabrication for most of these materials involves multistep operations, including filtration, spray coating, and sputtering. Most importantly, these methods present challenges for the preparation of thin films at the atomic or molecular scale. Therefore, the understanding of performance of ultrathin-film-based MSCs remains challenge. Herein, a B/N-enriched polymer film is successfully prepared using the photoassisted interfacial approach. The as-synthesized polymer film exhibits typical semiconductive characteristics and can be easily scaled up to a large area of up to tens of square centimeters. This ultrathin polymer film can be directly transferred to silicon wafers to fabricate MSC through laser scribing. The prepared MSC exhibits specific volumetric capacitance as high as 20.9 F cm-3, corresponding to volumetric energy density of 2.9 mWh cm-3 (at 0.1 V s-1). Moreover, the volumetric power density can reach 1461 W cm-3, surpassing most existing semiconductive polymer film-based MSC devices. In addition, the prepared MSC exhibits typical AC line-filtering ability (-67° at 120 Hz). This study offers a facile interfacial approach to preparing semiconductive polymer films with aromatic moieties for microsized energy storage devices.

Quinone-Enriched Conjugated Microporous Polymer as an Organic Cathode for Li-Ion Batteries.

Among various organic cathode materials, C═O group-enriched structures have attracted wide attention worldwide. However, small organic molecules have long suffered from dissolving in electrolytes during charge-discharge cycles. π-Conjugated microporous polymers (CMPs) become one solution to address this issue. However, the synthesis strategy for CMPs with rich C═O groups and stable backbones remains a challenge. In this study, a novel CMP enriched with C═O units was synthesized through a highly efficient Diels-Alder reaction. The as-prepared CMP exhibited a fused carbon backbone and a semiconductive characteristic with a band gap of 1.4 eV. When used as an organic electrode material in LIBs, the insoluble and robust fused structure caused such CMPs to exhibit remarkable cycling stability (a 96.1% capacity retention at 0.2 A g-1 after 200 cycles and a 94.8% capacity retention at 1 A g-1 after 1500 cycles), superior lithium-ion diffusion coefficient (5.30 × 10-11 cm2 s-1), and excellent rate capability (95.8 mAh g-1 at 1 A g-1). This study provided a novel synthetic method for fabricating quinone-enriched fused CMPs, which can be used as LIB cathode materials.

A Novel Heterostructure Based on RuMo Nanoalloys and N-doped Carbon as an Efficient Electrocatalyst for the Hydrogen Evolution Reaction.

Heterostructures exhibit considerable potential in the field of energy conversion due to their excellent interfacial charge states in tuning the electronic properties of different components to promote catalytic activity. However, the rational preparation of heterostructures with highly active heterosurfaces remains a challenge because of the difficulty in component tuning, morphology control, and active site determination. Herein, a novel heterostructure based on a combination of RuMo nanoalloys and hexagonal N-doped carbon nanosheets is designed and synthesized. In this protocol, metal-containing anions and layered double hydroxides are employed to control the components and morphology of heterostructures, respectively. Accordingly, the as-made RuMo-nanoalloys-embedded hexagonal porous carbon nanosheets are promising for the hydrogen evolution reaction (HER), resulting in an extremely small overpotential (18 mV), an ultralow Tafel slope (25 mV dec-1 ), and a high turnover frequency (3.57 H2 s-1 ) in alkaline media, outperforming current Ru-based electrocatalysts. First-principle calculations based on typical 2D N-doped carbon/RuMo nanoalloys heterostructures demonstrate that introducing N and Mo atoms into C and Ru lattices, respectively, triggers electron accumulation/depletion regions at the heterosurface and consequently reduces the energy barrier for the HER. This work presents a convenient method for rational fabrication of carbon-metal heterostructures for highly efficient electrocatalysis.

A coronene-based semiconducting two-dimensional metal-organic framework with ferromagnetic behavior.

Metal-organic frameworks (MOFs) have so far been highlighted for their potential roles in catalysis, gas storage and separation. However, the realization of high electrical conductivity (>10-3 S cm-1) and magnetic ordering in MOFs will afford them new functions for spintronics, which remains relatively unexplored. Here, we demonstrate the synthesis of a two-dimensional MOF by solvothermal methods using perthiolated coronene as a ligand and planar iron-bis(dithiolene) as linkages enabling a full π-d conjugation. This 2D MOF exhibits a high electrical conductivity of ~10 S cm-1 at 300 K, which decreases upon cooling, suggesting a typical semiconductor nature. Magnetization and 57Fe Mössbauer experiments reveal the evolution of ferromagnetism within nanoscale magnetic clusters below 20 K, thus evidencing exchange interactions between the intermediate spin S = 3/2 iron(III) centers via the delocalized π electrons. Our results illustrate that conjugated 2D MOFs have potential as ferromagnetic semiconductors for application in spintronics.

Toward Activity Origin of Electrocatalytic Hydrogen Evolution Reaction on Carbon-Rich Crystalline Coordination Polymers.

The fundamental understanding of electrocatalytic active sites for hydrogen evolution reaction (HER) is significantly important for the development of metal complex involved carbon electrocatalysts with low kinetic barrier. Here, the MSx Ny (M = Fe, Co, and Ni, x/y are 2/2, 0/4, and 4/0, respectively) active centers are immobilized into ladder-type, highly crystalline coordination polymers as model carbon-rich electrocatalysts for H2 generation in acid solution. The electrocatalytic HER tests reveal that the coordination of metal, sulfur, and nitrogen synergistically facilitates the hydrogen ad-/desorption on MSx Ny catalysts, leading to enhanced HER kinetics. Toward the activity origin of MS2 N2 , the experimental and theoretical results disclose that the metal atoms are preferentially protonated and then the production of H2 is favored on the MN active sites after a heterocoupling step involving a N-bound proton and a metal-bound hydride. Moreover, the tuning of the metal centers in MS2 N2 leads to the HER performance in the order of FeS2 N2 > CoS2 N2 > NiS2 N2 . Thus, the understanding of the catalytic active sites provides strategies for the enhancement of the electrocatalytic activity by tailoring the ligands and metal centers to the desired function.

Molybdenum Carbide-Embedded Nitrogen-Doped Porous Carbon Nanosheets as Electrocatalysts for Water Splitting in Alkaline Media.

Molybdenum carbide (Mo2C) based catalysts were found to be one of the most promising electrocatalysts for hydrogen evolution reaction (HER) in acid media in comparison with Pt-based catalysts but were seldom investigated in alkaline media, probably due to the limited active sites, poor conductivity, and high energy barrier for water dissociation. In this work, Mo2C-embedded nitrogen-doped porous carbon nanosheets (Mo2C@2D-NPCs) were successfully achieved with the help of a convenient interfacial strategy. As a HER electrocatalyst in alkaline solution, Mo2C@2D-NPC exhibited an extremely low onset potential of ∼0 mV and a current density of 10 mA cm-2 at an overpotential of ∼45 mV, which is much lower than the values of most reported HER electrocatalysts and comparable to the noble metal catalyst Pt. In addition, the Tafel slope and the exchange current density of Mo2C@2D-NPC were 46 mV decade-1 and 1.14 × 10-3 A cm-2, respectively, outperforming the state-of-the-art metal-carbide-based electrocatalysts in alkaline media. Such excellent HER activity was attributed to the rich Mo2C/NPC heterostructures and synergistic contribution of nitrogen doping, outstanding conductivity of graphene, and abundant active sites at the heterostructures.

Immobilizing Molecular Metal Dithiolene-Diamine Complexes on 2D Metal-Organic Frameworks for Electrocatalytic H2 Production.

Carbon electrocatalysts consisting of metal complexes such as MNx or MSx are promising alternatives to high-cost Pt catalysts for the hydrogen evolution reaction (HER). However, the exact HER active sites remain elusive. Here, molecular metal dithiolene-diamine (MS2 N2 , M=Co and Ni), metal bis(dithiolene) (MS4 ), and metal bis(diamine) (MN4 ) complexes were selectively incorporated into carbon-rich 2D metal-organic frameworks (2D MOFs) as model carbon electrocatalysts. The 2D MOF single layers, powders, and composites with graphene were thus prepared and showed definite active sites for H2 generation. The electrocatalytic HER activity of the 2D MOF-based catalysts with different metal complexes follow the order of MS2 N2 >MN4 >MS4 . Moreover, the protonation preferentially occurred on the metal atoms, and the concomitant heterolytic elimination of H2 was favored on the M-N units in the MS2 N2 active centers. The results provide an in-depth understanding of the catalytic active sites, thus making way for the future development of metal complexes in carbon-rich electrode materials for energy generation.

Wafer-sized multifunctional polyimine-based two-dimensional conjugated polymers with high mechanical stiffness.

One of the key challenges in two-dimensional (2D) materials is to go beyond graphene, a prototype 2D polymer (2DP), and to synthesize its organic analogues with structural control at the atomic- or molecular-level. Here we show the successful preparation of porphyrin-containing monolayer and multilayer 2DPs through Schiff-base polycondensation reaction at an air-water and liquid-liquid interface, respectively. Both the monolayer and multilayer 2DPs have crystalline structures as indicated by selected area electron diffraction. The monolayer 2DP has a thickness of∼0.7 nm with a lateral size of 4-inch wafer, and it has a Young's modulus of 267±30 GPa. Notably, the monolayer 2DP functions as an active semiconducting layer in a thin film transistor, while the multilayer 2DP from cobalt-porphyrin monomer efficiently catalyses hydrogen generation from water. This work presents an advance in the synthesis of novel 2D materials for electronics and energy-related applications.

Supported and inserted monomeric niobium oxide species on/in silica: a molecular picture.

The geometry, energetic, and spectroscopic properties of molecular structures of silica-supported niobium oxide catalysts are studied using periodic density functional calculations (DFT) and compared with experimental data. The calculations are done for Nb oxide species inserted or grafted in/on an amorphous hydroxylated silica surface. Different positions of the Nb atom/atoms in the silica structure have been investigated. By means of DFT calculations the geometry and the degree of hydration of Nb oxide species with oxidation state +5 have been studied. The local Nb geometry depends on different parameters such as the number of Nb-O-Si groups vs. Nb-O-H groups, the formation of H bonds and the distance between Nb atoms. The interaction between the oxide and silanol groups occurs by formation of Si-O-Nb bonds with chemically and thermally stable Brønsted and Lewis acid sites. UV-Vis, reflection absorption infrared vibrational spectra (RAIRS) as well as various thermodynamic properties have also been investigated in order to get a better insight into the system studied and to provide support to possible experimental studies.

Ab initio simulations reveal that reaction dynamics strongly affect product selectivity for the cracking of alkanes over H-MFI.

Product selectivity of alkane cracking catalysis in the H-MFI zeolite is investigated using both static and dynamic first-principles quantum mechanics/molecular mechanics simulations. These simulations account for the electrostatic- and shape-selective interactions in the zeolite and provide enthalpic barriers that are closely comparable to experiment. Cracking transition states for n-pentane lead to a metastable intermediate (a local minimum with relatively small barriers to escape to deeper minima) where the proton is shared between two hydrocarbon fragments. The zeolite strongly stabilizes these carbocations compared to the gas phase, and the conversion of this intermediate to more stable species determines the product selectivity. Static reaction pathways on the potential energy surface starting from the metastable intermediate include a variety of possible conversions into more stable products. One-picosecond quasiclassical trajectory simulations performed at 773 K indicate that dynamic paths are substantially more diverse than the potential energy paths. Vibrational motion that is dynamically sampled after the cracking transition state causes spilling of the metastable intermediate into a variety of different products. A nearly 10-fold change in the branching ratio between C2/C3 cracking channels is found upon inclusion of post-transition-state dynamics, relative to static electronic structure calculations. Agreement with experiment is improved by the same factor. Because dynamical effects occur soon after passing through the rate-limiting transition state, it is the dynamics, and not only the potential energy barriers, that determine the catalytic selectivity. This study suggests that selectivity in zeolite catalysis is determined by high temperature pathways that differ significantly from 0 K potential surfaces.